Electrochemical reduction induced self-doping of Ti3+ for efficient water splitting performance on TiO2 based photoelectrodes

Zhonghai Zhang, Mohamed N. Hedhili, Haibo Zhu, Peng Wang

Research output: Contribution to journalArticlepeer-review

167 Scopus citations


Hetero-element doping (e.g., N, F, C) of TiO2 is inevitably accompanied by significantly increased structural defects due to the dopants' nature being foreign impurities. Very recently, in situ self-doping with homo-species (e.g., Ti3+) has been emerging as a rational solution to enhance TiO2 photoactivity within both UV and visible light regions. Herein we demonstrate that conventional electrochemical reduction is indeed a facile and effective strategy to induce in situ self-doping of Ti3+ into TiO2 and the self-doped TiO2 photoelectrodes showed remarkably improved and very stable water splitting performance. In this study, hierarchical TiO2 nanotube arrays (TiO2 NTs) were chosen as TiO2 substrates and then electrochemically reduced under varying conditions to produce Ti3+ self-doped TiO2 NTs (ECR-TiO2 NTs). The optimized saturation photocurrent density and photoconversion efficiency on the ECR-TiO2 NTs under simulated AM 1.5G illumination were identified to be 2.8 mA cm-2 at 1.23 V vs. RHE and 1.27% respectively, which are the highest values ever reported for TiO 2 based photoelectrodes. The electrochemical impedance spectra measurement confirms that the electrochemical induced Ti3+ self-doping improved the electrical conductivity of the ECR-TiO2 NTs. The versatility and effectiveness of the electrochemical reduction method for Ti3+ self-doping in P25 based TiO2 was also examined and confirmed. This journal is © 2013 the Owner Societies.
Original languageEnglish (US)
Pages (from-to)15637
JournalPhysical Chemistry Chemical Physics
Issue number37
StatePublished - 2013

ASJC Scopus subject areas

  • General Physics and Astronomy
  • Physical and Theoretical Chemistry


Dive into the research topics of 'Electrochemical reduction induced self-doping of Ti3+ for efficient water splitting performance on TiO2 based photoelectrodes'. Together they form a unique fingerprint.

Cite this