Gas permeability, diffusivity, solubility, and aging characteristics of 6FDA-durene polyimide membranes

We have determined the intrinsic gas transport properties of He, H₂, O₂, N₂, CH₄, and CO₂ for a 6FDA-durene polyimide as a function of pressure, temperature and aging time. The permeability coefficients of O₂, N₂, CH₄, and CO₂ decrease slightly with increasing pressure. The pressure-dependent diffusion coefficients and solubility coefficients are consistent with the dual-sorption model and partial immobilization. All the gas permeabilities increase with temperature and their apparent activation energies for permeation increase with increasing gas molecular sizes in the order of CO₂, O₂, N₂, and CH₄.The percentages of permeability decay after 280 days of aging are 22, 32, 36, 40, 42, and 30% for He, H₂, O₂, N₂, CH₄, and CO₂, respectively. Interestingly, except for H₂ (kinetic diameter of 2.89Å), the percentages of permeability decay increase exactly in the order of He (kinetic diameter of 2.6Å), CO₂ (3.30Å), O₂ (3.46Å), N₂ (3.64Å), and CH₄ (3.80Å). The apparent activation energies of permeation for O₂, N₂, CH₄, and CO₂ increase with aging because of the increases in activation energies of diffusion and the decreases in solubility coefficients. The activation-energy increase for diffusion is probably due to the decrease in polymeric molar volume because of densification during aging. The reduction in solubility coefficient indicates the available sites for sorption decreasing with aging because of the reduction of microvoids and interstitial chain space.