Nb-doped TiO2 cathode catalysts for oxygen reduction reaction of polymer electrolyte fuel cells

Takuya Arashi, Jeongsuk Seo, Kazuhiro Takanabe, Jun Kubota, Kazunari Domen

Research output: Contribution to journalArticlepeer-review

24 Scopus citations


Nb-doped TiO2 particles were studied as electrocatalysts for the oxygen reduction reaction (ORR) under acidic conditions. The Nb-doped TiN nanoparticles were first synthesized by meso-porous C3N4 and then fully oxidized to Nb-doped TiO2 by immersing in 0.1 M H 2SO4 at 353 K for 24 h. Although the ORR activity of the as-obtained sample was low, a H2 treatment at relatively high temperature (1173 K) dramatically improved the ORR performance. An onset potential as high as 0.82 VRHE was measured. No degradation of the catalysts was observed during the oxidation-reduction cycles under the ORR condition for over 127 h. H2 treatment at temperatures above 1173 K caused the formation of a Ti4O7 phase, resulting in a decrease in ORR current. Elemental analysis indicated that the Nb-doped TiO 2 contained 25 wt% residual carbon. Calcination in air at 673 or 973 K eliminated the residual carbon in the catalyst, which was accompanied by a dramatic decrease in ORR activity. This post-calcination process may reduce the conductivity of the sample by filling the oxygen vacancies, and the carbon residue in the particle aggregates may enhance the electrocatalytic activity for ORR. The feasibility of using conductive oxide materials as electrocatalysts is discussed. © 2013 Elsevier B.V.
Original languageEnglish (US)
Pages (from-to)181-186
Number of pages6
JournalCatalysis Today
StatePublished - Sep 2014

ASJC Scopus subject areas

  • General Chemistry
  • Catalysis


Dive into the research topics of 'Nb-doped TiO2 cathode catalysts for oxygen reduction reaction of polymer electrolyte fuel cells'. Together they form a unique fingerprint.

Cite this